Virgin & Recycled linear low density polyethylene (LLDPE)
LLDPE Resin Powder / LLDPE Granule
1.Grade:
LLDPE Film Grade/
Blowing moulding grade/
Injection grade/
Extrusion grade/
Pipe grade/
Rotational Molding Grade / Roto-moulding grade
2. Specification :
a. different MFR or MFI are available for your different usage.
b. good quality and reasonable price
c. non-poteonods no smell adurless
d. it can replaced original plastic material, sometimes it can replace new material
A. LLDPE film grade
Tests | Value | Unit |
Melt Flow Rate (MFR) | 2.0±0.4 | g/10min |
Density | 920±2 | Kg/cm3 |
Tensile Strengthat Yield | 8 | Mpa ≥ |
Tensile Strengthat Break | 12 | Mpa ≥ |
haze | 15 | %≤ |
Packing | In 25 kg PP woven bags,20MT/20’FCL | |
B. LLDPE for Master Batch Use
Tests | Value | Unit |
Melt Flow Rate (MFR) | 20 | g/10min |
Density | 0.924 | g/cm3 |
Tensile Strength | MD12 | Mpa |
TD 10 | ||
Elongation at Yield | 13 | % |
Elongation at Break | 200 | |
Dark Drop Impact | 105 | g |
Brittle Temperature(F 50) | -70 | °C |
Vicat Softening Point | 90 | °C |
Packing | In 25 kg PP woven bags,20MT/20’FCL | |
C.LLDPE Powder Rotational Molding Grade for Tank Use
Tests | Value | Unit |
Melt Flow Rate (MFR) | 3.2 | g/10min |
Density | 0.939 | g/cm3 |
Melting Point | 127 | °C |
Tensile Yield Strength | 21 | Mpa |
Tensile Strength at Break | 28 | Mpa |
Elongation at Break | 1,100 | % |
Flexural Modulus | 750 | Mpa |
Brittle Temperature | <-60 | °C |
3.Storage:
Shelf life: It should avoid damp, contaminated and direct sun light during transport.And should be stored in ventilated and dry place. Do not put it with flammable and corrosive substances together,and away from the fire.